DIN Hardness depth of heat-treated parts; determination of the effective depth of hardening after nitriding. standard by Deutsches. DIN – Draft standard [WITHDRAWN] DIN – Draft. Heat treatment of ferrous materials; terms. from EUR VAT. Standard [WITHDRAWN] DIN Hardness depth of heat-treated parts – Determination of the effective depth of carburized and.

Author: Tajind JoJozragore
Country: Samoa
Language: English (Spanish)
Genre: Business
Published (Last): 1 May 2015
Pages: 473
PDF File Size: 17.74 Mb
ePub File Size: 3.73 Mb
ISBN: 990-4-48398-667-8
Downloads: 47777
Price: Free* [*Free Regsitration Required]
Uploader: Kazinos

Similar to the Vickers method the calculation of the hardness is based on the ratio of the average diagonal diameter for the used ball and the test load. Different materials like plastics, metals, coatings and ceramics can be tested. The software automatically assigns colors for the minimum and maximum hardness values. Also in the field of damage investigation hardness profile measurements are used, to e. From the hardness test procedures, the Vickers method is the most universally applicable test.

Hardness mapping are often applied to verify welded joints.

Thermal and mechanical stress can induce microstructural changes in materials, which can be detected with a hardness test. Furthermore it offers the possibility to determine values, which are equivalent compared to the traditional methods.

GWP: Hardness test

With the micro hardness test usually load ranges of dib to g e. Filling the sample with indents hardness mapping can be useful for case-hardened parts or to check sample homogeneity. The GWP is equipped with the most modern hardness test devices, which offer the possibilities of manual, semiautomatic and fully automatic evaluation.


Because of this kind of determination the hardness value can be read from a scale without optical measurement devices and the requirements regarding surface quality are lower. Our according to DIN EN ISO accredited lab offers the usual stationary methods of hardness testing, which are used in the field of metallic materials: The Brinell hardness test is used for soft to medium hard metals, and very porous and inhomogeneous materials such as cast or light metal alloys.

This ddin is used to detect even the smallest local don increase in large samples. The Rockwell method is preferably used for very hard materials or heat treatment conditions, e. By these small impressions also very close contiguous impressions can be realized e.

For the examination next to metallographic investigations also hardness profiles are used. These evaluations lead to conclusions about e.

Hardness test with metals. Usually the examinations take place on metallographic prepared samples. In contrast to the Vickers and Brinell method, the hardness is determined not by the lasting dent diagonal but by the depth of penetration. The typical load range extends from 0.

For this purpose several Vickers-test indentations are set and measured in defined intervals to the component edge. Modern dun materials offer a very wide range of different operation purposes. Hardness mapping are performed according to Vickers.


Particularly in the case of multi-layered welds, it is thus possible to identify specific areas, in which the heat input has significantly affected the microstructure, and as consequence affects the quality of the weld joint.

In the tests hard metal balls with different diameters 1, 2. The GWP covers with their equipment park the typical testing areas. Vickers, Rockwell and Brinell.

Hardness test

Hereby a pyramidal diamond indenter is pressed with a defined stress dim the workpiece. Instrumented penetration testing universal hardness test. For the characterization of different materials the hardness test offers a very wide spectrum of possibilities. Starting from very soft non-ferrous metals such as Pb or Cu, over surface layer hardened steels up to very hard coatings such as tungsten carbide.

Thus, the hardness is an essential ingredient of component calculations, drawing specifications or in the characterization of materials. Via these measurements next to the hardness difference compared to the core hardness also the depth can be determined.

A determination of the hardniss is carried out, depending on the selected test load, on the by plastic deformation caused dent by average calculation of the diagonal.